Polymaker Fiberon™ PA612-CF15 Black - 1.75mm - 3Kg

Ref. FG07002

The Polymaker Fiberon™ PA612-CF15 filament is a high-quality material reinforced with 15% carbon fibers, designed for applications that require both lightness and robustness. This filament, composed of nylon PA6 and PA12, offers exceptional performance for the production of mechanical and functional parts.

3kg spool, filament with a diameter of 1.75mm. Formerly known as PolyMide PA612-CF.

  • Integrated carbon fibers for enhanced impact resistance and wear resistance.
  • Ideal for parts subjected to high temperatures (175°C).
  • Low deformation for dimensionally stable parts.
€169.16 excl. VAT

VAT at 20%, which is €202.99 TTC including tax.

Pre Order Free shipping
Get an instant quote

Our experts are at your service to answer your questions and provide advice at info@polyfab3d.com.

Delivery within 48/72 hours

Order before 1pm. Same day shipping

Free delivery

Free delivery near you from €69.90

Premium support

Our teams are on hand to answer all your questions

Over 2000 products

A wide choice of products from the biggest brands

Polymaker Fiberon™ PA612-CF15 Black - 1.75mm - 3Kg

The Polymaker Fiberon™ PA612-CF15 filament is a hybrid material combining nylon PA612 with 15% carbon fibers, offering a combination of lightness, strength, and thermal stability. It is particularly suitable for demanding industrial applications, allowing the creation of functional parts requiring both high mechanical strength and optimal printing precision.

With the integration of carbon fibers, this filament stands out for its increased rigidity and remarkable wear resistance. It also minimizes deformation during printing, ensuring strong and dimensionally stable parts. It is highly recommended for manufacturing mechanical components, moving parts, or tools in technical and industrial environments.

Advantages of Polymaker Fiberon™ PA612-CF15

  • 15% carbon fibers: Provides superior strength and enhanced resistance while maintaining low density for lightweight and dynamic applications.
  • Excellent thermal resistance: Withstands high temperatures (175°C), ideal for applications where heat is a stress factor for materials.
  • Low warping: Thanks to its characteristics, it ensures precise, stable, and deformation-free printing.
  • Lightweight: Lighter than other composites, this filament is perfect for projects requiring weight management without sacrificing performance.

Printing Recommendations

  • Extrusion temperature: 250-300°C to ensure perfect material fusion.
  • Bed temperature: 40-50°C to ensure good adhesion of the first layer.
  • Recommended nozzle: Use a hardened steel or ruby nozzle to prevent premature wear due to the carbon fibers in the filament. Metal hotend for printing above 280°C required.
  • Printing speed: Up to 300 mm/s.
  • Storage: Store the filament in a dry environment. If the environment is humid, dry the filament before use (100°C for 10 hours in a conventional oven or 18h at level 3 with the PolyDryer).
  • Post-print annealing: Annealing at 100°C for 10 hours improves the mechanical strength of the parts.
  • 🎯 We collaborate with businesses.
  • 📦 Stock in Europe
  • 🚚 Ships within 24 hours
  • 🔐 Secure payments
  • 🔙 14 days to change your mind
  • 📱 Need advices ? Contact technical support

A question? Need help? Contact us, it's a pleasure to help you.

✉️ Contact us

Our team is available from Monday to Friday, from 10 am to 12 pm and from 2 pm to 5 pm.

Specifications for Polymaker Fiberon™ PA612-CF15 Black - 1.75mm - 3Kg

Technologie / Produit

Technology
FDM
Material
PA
Visual aspect
Opaque
Diameter
1.75 mm
Sensitivity to humidity
Strong
Application
Prototyping, Production, Functional part
Odour
Yes
Harmful
Yes
Level of difficulty
Intermediate
Brand
Polymaker
Type of product
3D Filament
Colour
Black
Net weight
3 kg

Valeurs techniques

Deflection temperature under load (0.45 MPa)
175 °C
Deflection temperature under load (1.8 MPa)
114 °C
Temperature VICAT
206,2 °C
Charpy
7 kJ/m² of energy
Resistors
Mechanical engineering
Tensile modulus
4736 Mpa
Flexural modulus
4331 Mpa
Maximum elongation at break
3 %
Density
1.03 g/cm3

Extrusion

Nozzle type
Tempered steel, Ruby
Type of consumable
Non-proprietary filament (open system)
Min. plateau temperature
40 °C
Max. tray temperature
50 °C
Min. extrusion temperature
250 °C
Max. extrusion temperature
300 °C
Min. speed
30 mm/s
Max. speed
300 mm/s
Minimum nozzle diameter
0.5 mm
Bowden compatibility
Yes
Warping sensitivity
Low
AMS compatible
No

Équipements spécifiques

Closed printing enclosure
Yes
Filtration
HEPA, Coal

Installation / Prérequis

Type
Filament on spool
Box supplied
Yes
Coil material
Cardboard

Customer reviews about Polymaker Fiberon™ PA612-CF15 Black - 1.75mm - 3Kg

You might also like

Product added to wishlist