Polymaker Fiberon™ PPS-CF10 Black - 1.75mm - 3Kg

Ref. FM01002

The Polymaker Fiberon™ PPS-CF10 filament, a material reinforced with 10% carbon fibers. Ideal for demanding applications, it combines exceptional thermal resistance and great dimensional stability.

3kg spool, 1.75mm diameter filament.

  • Carbon fiber reinforcement (10%) for increased rigidity and durability.
  • High thermal resistance, withstands temperatures up to 252.5°C.
  • Flame retardant filament: V0 UL94.
  • Excellent resistance to chemicals and wear.
  • Low deformation during printing for high precision results.
€337.49 excl. VAT

VAT at 20%, which is €404.99 TTC including tax.

Pre Order Free shipping
Get an instant quote

Our experts are at your service to answer your questions and provide advice at info@polyfab3d.com.

Delivery within 48/72 hours

Order before 1pm. Same day shipping

Free delivery

Free delivery near you from €69.90

Premium support

Our teams are on hand to answer all your questions

Over 2000 products

A wide choice of products from the biggest brands

Polymaker Fiberon™ PPS-CF10 Black - 1.75mm - 3Kg

The Polymaker Fiberon™ PPS-CF10 filament incorporates 10% carbon fibers into a PPS (Polyphenylene Sulfide) polymer, an exceptionally strong and stable material under extreme conditions. This filament is designed to meet the needs of industrial applications, especially those exposed to high temperatures, aggressive chemicals, and significant mechanical loads.

Due to its reinforced composition, it combines excellent heat resistance, remarkable dimensional stability, and low deformation during printing.

The Polymaker Fiberon™ PPS-CF10 is particularly suitable for the production of functional parts that require high-performance characteristics, such as automotive components, tools, or parts of devices subjected to severe conditions. Its low moisture absorption and wear resistance also make it an ideal choice for durable and demanding applications.

Features of Polymaker Fiberon™ PPS-CF10

  • Carbon fibers (10%): Enhances material rigidity and strength while maintaining lightness for mobile and complex applications.
  • Excellent thermal resistance: Capable of withstanding temperatures up to 252.5°C without deformation, ideal for parts exposed to thermally aggressive environments.
  • Chemical resistance: PPS is particularly suitable for environments containing aggressive chemicals (acids, alkalis, fuels, and solvents), offering exceptional durability.
  • Low deformation during printing: Ensures superior printing accuracy, with optimal dimensional stability and low warping tendency.

Printing Tips

  • Extrusion temperature: 310-350°C for optimal filament melting.
  • Bed temperature: 80-90°C to ensure good first layer adhesion.
  • Printing speed: up to 300 mm/s.
  • Use of a hardened steel nozzle: Carbon fibers can quickly wear out standard nozzles, so it is recommended to use reinforced nozzles. Metal hotend for printing above 310°C is necessary.
  • Drying: Store the filament in a dry environment or dry it at 100°C for 10 hours before use to prevent moisture absorption. Use of the PolyDryer at level 3 for 18 hours is possible.
  • 🎯 We collaborate with businesses.
  • 📦 Stock in Europe
  • 🚚 Ships within 24 hours
  • 🔐 Secure payments
  • 🔙 14 days to change your mind
  • 📱 Need advices ? Contact technical support

A question? Need help? Contact us, it's a pleasure to help you.

✉️ Contact us

Our team is available from Monday to Friday, from 10 am to 12 pm and from 2 pm to 5 pm.

Specifications for Polymaker Fiberon™ PPS-CF10 Black - 1.75mm - 3Kg

Technologie / Produit

Technology
FDM
Material
PPS
Visual aspect
Opaque
Diameter
1.75 mm
Sensitivity to humidity
Low
Application
Prototyping, Production, Functional part
Odour
Yes
Harmful
Yes
Level of difficulty
Intermediate
Brand
Polymaker
Type of product
3D Filament
Colour
Black
Net weight
3 kg

Valeurs techniques

Glass transition temperature
98 °C
Deflection temperature under load (0.45 MPa)
253 °C
Deflection temperature under load (1.8 MPa)
133 °C
Temperature VICAT
268 °C
Charpy
5 kJ/m² of energy
Resistors
Mechanical engineering, Chemical
Tensile modulus
5314 Mpa
Flexural modulus
4647 Mpa
Maximum elongation at break
1 %
Density
1.29 g/cm3

Extrusion

Nozzle type
Tempered steel, Ruby
Type of consumable
Non-proprietary filament (open system)
Min. plateau temperature
80 °C
Max. tray temperature
90 °C
Min. extrusion temperature
310 °C
Max. extrusion temperature
350 °C
Min. speed
30 mm/s
Max. speed
300 mm/s
Minimum nozzle diameter
0.5 mm
Bowden compatibility
Yes
Warping sensitivity
Average
AMS compatible
No

Équipements spécifiques

Closed printing enclosure
Yes
Filtration
HEPA, Coal

Installation / Prérequis

Type
Filament on spool
Box supplied
Yes
Coil material
Cardboard

Customer reviews about Polymaker Fiberon™ PPS-CF10 Black - 1.75mm - 3Kg

You might also like

Product added to wishlist